Growth of a Bonelike Apatite on Chitosan Microparticles After a Calcium Silicate Treatment

last updated: 2013-02-25
TitleGrowth of a Bonelike Apatite on Chitosan Microparticles After a Calcium Silicate Treatment
Publication TypePapers in Scientific Journals
Year of Publication2008
AuthorsLeonor I. B., Baran E. T., Kawashita M., Reis R. L., Kokubo T., and Nakamura T.

Bioactive chitosan microparticles can be prepared Successfully by treating them with a calcium silicate solution and then subsequently soaking them in simulated body fluid (SBF). Such a combination enables the development of bioactive microparticles that can be used for several applications in the medical field, including injectable biomaterial systems and tissue engineering carrier systems. Chitosan microparticles. 0.6 mu m in average size, were soaked either for 12 h in fresh calcium silicate solution (condition I) or for 1 h in calcium silicate solution that had been aged for 24 h before use (condition II). Afterwards, they were dried in air at 60 degrees C for 24 h. The samples were then soaked in SBF for 1, 3 and 7 days. After the condition I calcium silicate treatment and the Subsequent soaking in SBF, the microparticles formed a dense apatite layer after only 7 days of immersion, which is believed to be due to the formation of silanol (Si-OH) groups effective for apatite formation. For condition II, the microparticles successfully formed an apatite layer oil their Surfaces in SBF within only 1 day of immersion. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

JournalActa Biomaterialia
Date Published2008-09-01
DOI 10.1016/j.actbio.2008.03.003
Keywordsapatite, Biomimetic process, Calcium silicate, Chitosan, microparticles