Preparation and characterization of macro/micro porous silk fibroin /nano-sized calcium phosphate scaffolds for bone tissue engineering

last updated: 2013-04-16
TitlePreparation and characterization of macro/micro porous silk fibroin /nano-sized calcium phosphate scaffolds for bone tissue engineering
Publication TypeConference Abstract -ISI Web of Science Indexed
Year of Publication2012
AuthorsYan L. P., Correia C., Silva-Correia J., Caridade S. G., Fernandes E. M., Mano J. F., Sousa R. A., Dr. Oliveira J. M., Oliveira A. L., and Reis R. L.
Abstract


Macro/micro porous silk scaffolds with nano-sized calcium phosphate (CaP) particles were developed for bone tissue engineering. Different amounts of nano-sized CaP particles 4, 8, 16 and 25% (CaP:silk fibroin, wt/wt) were generated into the highly concentrated aqueous silk fibroin solutions via an in-situ approach. Afterwards, the pure silk and silk/nano-CaP porous scaffolds were produced by a combina- tion of salt-leaching/freeze-drying methods. Thermal gravimetric analysis results were able to demonstrated that the silk/nano-CaP scaffolds maintained 64–87% of incorporated CaP after salt-leaching. Dynamic mechanical analysis showed that storage modulus of the 16% formulation was significantly higher than all remaining groups. The porosity of silk/nano-CaP scaffolds assessed using Micro-Com- puted Tomography decreased from 79.8% to 63.6% with increasing CaP incorporated until 16%. By soaking the scaffolds in Simulated Body Fluid for 7 days, cauliflower-like apatite clusters were observed on the surface of both macro and micro pores of 16% and 25% for- mulations, which was not observed in 4 and 8% formulations. 16% silk/nano-CaP scaffolds were further chosen for in vitro cytotoxicity and biocompatibility assays. Both silk and 16% silk/nano-CaP scaf- folds were non-cytotoxic and promoted cell adhesion and prolifera- tion to a similar extent. These results indicated that the 16% silk/ nano-CaP scaffolds could be a good candidate for bone tissue engineering.

JournalJournal of tissue engineering and regenerative medicine
Volume6
IssueSuppl.1
Pagination181
Date Published2012-09-30
PublisherJohn Wiley & Sons
Conference Location3rd TERMIS World Congress 2012, 5-8 September 2012, Vienna, Austria
DOI10.1002/term.1586
Keywordsbone, Silk Fibroin